文章信息/Info
- Title:
- Influence and Thermodynamic Analysis of Calcium Treatment on Inclusions in 2205 Duplex Stainless Steel
- 文章编号:
- 1002-1639(2017)04-0018-04
- 作者:
- 刘 崇1; 2; 刘润藻1; 2; 宋水根3; 朱 荣1; 2; 王宝华1; 2; 4; 沈 汉5
- 1. 北京科技大学冶金与生态工程学院,北京 100083;2. 高端金属特种熔炼与制备北京市重点实验室,北京 100083;
3. 新余新良特殊钢有限责任公司,江苏 新余 338013;4. 河北钢铁集团承德分公司,河北 承德 067002;5. 万宝矿产有限公司,北京 100083
- Author(s):
- LIU Chong1; 2; LIU Runzao1; 2; Song Shuigen3; ZHU Rong1; 2; WANG Baohua1; 2; 4; SHEN Han5
- 1. School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beijing 100083,China; 2. Beijing Key Laboratory of Special Melting and Preparation of High-end Metal Materials, Beijing 100083,China; 3. Xinyu Xinliang Special Steel Co.Ltd., Xinyu 338013, China; 4. Chengde Steel Company of Heibei Steel Company Group,Chengde 067002,China;5. Wanbao Mining Co.Ltd. Beijing 100083, China
- 关键词:
- 夹杂物; 钙处理; 热力学
- 分类号:
- TF764.1
- DOI:
- 10.3969/j. issn. 1002-1639.2017.04.005
- 文献标识码:
- A
- 摘要:
- 针对某钢厂2205双相不锈钢的生产工艺,取钙处理前后的钢样,研究钙处理对夹杂变性的效果。实验表明:钙处理后钢中的Al2O3、MgO-Al2O3夹杂物逐渐演变为MgO-Al2O3-CaO-(CaS),部分处于1 873 K温度下的液相区内,夹杂物的形状更加规则,但是还有少数的夹杂物变性效果不理想。通过热力学计算,得到了1 873 K时的Ca-Al、Al-S平衡曲线,得出了为避免生成固态铝酸钙、CaS理论上应满足的条件:即将w([Ca])、w([Al])含量控制在C12A7曲线附近。